TangoBlack and TangoGray and TangoPlus rubber like flexible materials enable models that closely resemble the “feel” of flexible target products, opening new business opportunities for Eden systems. They are particularly ideal for many consumer electronics applications, shoes, toys, general industrial applications, and rapid tooling.
Please, find the complete FullCure® Tango family data charts below:
|
FullCure®970 TangoBlack
|
|
Property |
ASTM |
Results (Metric) |
Results (Imperial) |
|
Tensile Strength |
D-412 |
MPa |
2 |
psi |
290 |
|
Elongation at Break |
D-412 |
% |
47.7 |
% |
47.7 |
|
Compressive Set |
D-395 |
% |
0.8 |
% |
1 |
|
Shore A Hardness |
D-2240 |
Scale A |
61 |
Scale A |
61 |
|
Tensile Tear Resistance |
D-624 |
Kg/cm |
3.8 |
Lb/in |
21 |
|
Tg |
DSC
(-80ºC+100ºC) |
ºC |
-10.7 |
ºF |
13 |
|
|
|
|
|
|
|
|
|
|
|
|
| FullCure®950 TangoGray |
|
Property |
ASTM |
Results (Metric) |
Results (Imperial) |
|
Tensile Strength |
D-412 |
MPa |
4.36 |
psi |
632 |
|
Elongation at Break |
D-412 |
% |
47 |
% |
47.0 |
|
Compressive Set |
D-395 |
% |
1 |
% |
1 |
|
Shore A Hardness |
D-2240 |
Scale A |
75 |
Scale A |
75 |
|
Tensile Tear Resistance |
D-624 |
Kg/cm |
9.5 |
Lb/in |
54 |
|
Tg |
DSC
(-80ºC+100ºC) |
ºC |
2.6 |
ºF |
37 |
|
|
|
|
|
|
|
|
|
|
|
|
| FullCure®930 TangoPlus |
|
Property |
ASTM |
Results (Metric) |
Results (Imperial) |
|
Tensile Strength at Break |
D-412 |
MPa |
1.455 |
psi |
211 |
|
Tenslie Modulus at 20% Strain |
D-413 |
MPa |
0.146 |
psi |
21 |
|
Tenslie Modulus at 30% Strain |
D-414 |
MPa |
0.185 |
psi |
27 |
|
Tenslie Modulus at 50% Strain |
D-415 |
MPa |
0.263 |
psi |
38 |
|
Elongation at Break |
D-412 |
% |
218 |
% |
218.0 |
|
Compressive Set, 22 Hr, 750C |
D-395 |
% |
4.4 |
% |
4 |
|
Shore A Hardness |
D-2240 |
Scale D |
27 |
Scale D |
27 |
|
Ross Flex |
D-1052 |
|
Above 150,000 |
|
Above 150,000 |
|
Tensile Tear Resistance |
D-624 |
Kg/cm |
3.47 |
Lb/in |
20 |
| Tg |
DSC
(-80ºC+100ºC) |
ºC |
-9.6 |
ºF |
15 |