Untitled Document
The Vero family provides users of Eden systems with the ability to produce
opaque models that closely resemble the “look” of the target products.
Please, find the complete FullCure® Vero Family Data Charts Below:
|
FullCure®830 VeroWhite |
| Property |
ASTM |
Results (Metric) |
Results (Imperial) |
| Tensile Strength |
D-638-03 |
MPa |
49.8 |
psi |
7,221 |
| Modulus of Elasticity |
D-638-04 |
MPa |
2,495 |
psi |
361,775 |
| Elongation at Break |
D-638-05 |
% |
20 |
% |
20 |
| Flexural Strength |
D-790-03 |
MPa |
74.6 |
psi |
10,817 |
| Flexural Modulus |
D-790-04 |
MPa |
2,137 |
psi |
309,865 |
| Izod Notched Impact |
D-256-06 |
J/m |
24.1 |
ft lb/in |
0.45 |
| Shore Hardness |
Scale D |
Scale D |
83 |
Scale D |
83 |
| Rockwell Hardness |
Scale M |
Scale M |
81 |
Scale M |
81 |
| HDT at 0.45 MPa |
D-648-06 |
ºC |
47.6 |
ºF |
118 |
| HDT at 1.82MPa |
D-648-07 |
ºC |
43.6 |
ºF |
110 |
| Tg |
DMA, E" |
ºC |
58 |
ºF |
136 |
| Ash Content |
NA |
% |
<0.4 |
% |
<0.4 |
| Water Absorption |
D570-98 24 Hr |
% |
1.47 |
% |
1.47 |
|
|
|
|
|
|
|
|
|
|
|
|
| FullCure®840 VeroBlue |
| Property |
ASTM |
Results (Metric) |
Results (Imperial) |
| Tensile Strength |
D-638-03 |
MPa |
55.1 |
psi |
7,990 |
| Modulus of Elasticity |
D-638-04 |
MPa |
2,740 |
psi |
397,300 |
| Elongation at Break |
D-638-05 |
% |
20 |
% |
20 |
| Flexural Strength |
D-790-03 |
MPa |
83.6 |
psi |
12,122 |
| Flexural Modulus |
D-790-04 |
MPa |
1,983 |
psi |
287,535 |
| Compressive Strength |
D-695-02 |
MPa |
79.3 |
psi |
11,499 |
| Izod Notched Impact |
D-256-06 |
J/m |
23.6 |
ft lb/in |
0.44 |
| Shore Hardness |
Scale D |
Scale D |
83 |
Scale D |
83 |
| Rockwell Hardness |
Scale M |
Scale M |
81 |
Scale M |
81 |
| HDT at 0.45 MPa |
D-648-06 |
ºC |
48.8 |
ºF |
120 |
| HDT at 1.82MPa |
D-648-07 |
ºC |
44.8 |
ºF |
113 |
| Tg |
DMA, E" |
ºC |
48.7 |
ºF |
120 |
| Ash Content |
NA |
% |
<0.3 |
% |
<0.3 |
| Water Absorption |
D570-98 24 Hr |
% |
1.87 |
% |
1.87 |
|
|
|
|
|
|
|
|
|
|
|
|
| FullCure®870 VeroBlack |
| Property |
ASTM |
Results (Metric) |
Results (Imperial) |
| Tensile Strength |
D-638-03 |
MPa |
50.7 |
psi |
7,352 |
| Modulus of Elasticity |
D-638-04 |
MPa |
2,192 |
psi |
317,840 |
| Elongation at Break |
D-638-05 |
% |
17.7 |
% |
18 |
| Flexural Strength |
D-790-03 |
MPa |
79.6 |
psi |
11,542 |
| Flexural Modulus |
D-790-04 |
MPa |
2,276 |
psi |
330,020 |
| Izod Notched Impact |
D-256-06 |
J/m |
23.9 |
ft lb/in |
0.45 |
| Shore Hardness |
Scale D |
Scale D |
83 |
Scale D |
83 |
| HDT at 0.45 MPa |
D-648-06 |
ºC |
47 |
ºF |
117 |
| HDT at 1.82MPa |
D-648-07 |
ºC |
42.9 |
ºF |
109 |
| Tg |
DMA, E" |
ºC |
62.7 |
ºF |
145 |