FullCure® Hearing Aid Family
|
|
|
| |
Using Objet Eden 3-D printers based on our unique PolyJet technology, you can manufacture hearing aid molds with maximum productivity and flexibility, at a minimum cost.
The Eden’s unique ability to build layers that are just 16 microns thin and the easily- removed gel-like support structure ensures ultra-smooth, unmarked flawlessly shaped surfaces that deliver perfect fit and comfort. The solution includes a choice of three resins designed especially for the unique needs of hearing aids: Clear, Rose Clear and Skin Tone.
Please, find the complete FullCure® Hearing Aid Family Data Charts Below:
|
FullCure®640 Clear |
| Property |
ASTM |
Results (Metric) |
Results (Imperial) |
|
Tensile Strength |
D-638-03 |
MPa |
43.1 |
psi |
6,250 |
| Modulus of Elasticity |
D-638-04 |
MPa |
1,931 |
psi |
279,995 |
| Elongation at break |
D-638-05 |
% |
18 |
% |
18 |
| Flexural Strength |
D-790-03 |
MPa |
63.2 |
psi |
9,164 |
| Flexural Modulus |
D-790-04 |
MPa |
1,833 |
psi |
265,785 |
| Izod Notched Impact |
D-256-06 |
J/m |
32.7 |
ft lb/in |
0.61 |
| Shore Hardness |
Scale D |
Scale D |
84 |
Scale |
84 |
| HDT at 0.45 MPa |
D-648-06 |
ºC |
46.1 |
ºF |
115 |
| HDT at 1.82 MPa |
D-648-07 |
ºC |
41.5 |
ºF |
107 |
| Tg |
DMA, E" |
|
63.3 |
ºF |
146 |
| Water Absorption |
D570-98 24Hrs |
% |
1.02 |
% |
1.02 |
|
FullCure®660 RoseClear |
| Property |
ASTM |
Results (Metric) |
Results (Imperial) |
| Tensile Strength |
D-638-03 |
MPa |
43.1 |
psi |
6,250 |
| Modulus of Elasticity |
D-638-04 |
MPa |
1,931 |
psi |
279,995 |
| Elongation at Break |
D-638-05 |
% |
18 |
% |
18 |
| Flexural Strength |
D-790-03 |
MPa |
63.2 |
psi |
9,164 |
| Flexural Modulus |
D-790-04 |
MPa |
1,833 |
psi |
265,785 |
| Izod Notched Impact |
D-256-06 |
J/m |
32.7 |
ft lb/in |
0.61 |
| Shore Hardness |
Scale D |
Scale D |
84 |
Scale D |
84 |
| HDT at 0.45 MPa |
D-648-06 |
|
46.1 |
ºF |
115 |
| HDT at 1.82 MPa |
D-648-07 |
ºC |
|
ºF |
107 |
| Tg |
DMA, E" |
ºC |
63.3 |
ºF |
146 |
| FullCure®680 SkinTone |
| Property |
ASTM |
Results (Metric) |
Results (Imperial) |
| Tensile Strength |
D-638-03 |
MPa |
56 |
psi |
8,120 |
| Modulus of Elasticity |
D-638-04 |
MPa |
2,700.6 |
psi |
391,587 |
| Elongation at Break |
D-638-05 |
% |
10.4 |
% |
10 |
| Flexural Strength |
D-790-03 |
MPa |
92.8 |
psi |
13,456 |
| Flexural Modulus |
D-790-04 |
MPa |
2,590 |
psi |
375,550 |
| Izod Notched Impact |
D-256-06 |
J/m |
22.2 |
ft lb/in |
0.42 |
| Shore Hardness |
Scale D |
Scale D |
85 |
Scale D |
85 |
| HDT at 0.45 MPa |
D-648-06 |
ºC |
56.5 |
ºF |
134 |
| HDT at 1.82 MPa |
D-648-07 |
ºC |
51.3 |
ºF |
124 |
| Tg |
DMA, E" |
ºC |
58.5 |
ºF |
137 |
|
|
|
|
|
|
| |
|